| PRODUCT | GRADE | EQUIVALENT STANDARD | CHEMICAL COMPOSITION (%) | SUPPLY CONDITION | APPLICATION | TYPE OF APPLICATION | ||||||||||
| AISI | DIN | JIS | C | Si | Mn | Cr | Mo | Ni | V | W | Oth. | |||||
| Duplex Stainless Steel | ||||||||||||||||
 | LDX 2101 | – | 1.4162, | – | 0.04 | 1.00 | 4.00-6.00 | 21.0-22.0 | 0.10-0.80 | 1.35-1.70 | – | – | P/0.04, S/0.03, Cu/0.10-0.80 | 290 HB | Lean duplex, good strength, resistant to fatigue-corrosion, generally use in the paper-power industries such as water treatment, water storage systems, storage tanks |  |
| 2205 | – | 1.4462, | SUS 329J3L | 0.03 | 1.00 | 2.00 | 21.0-23.0 | 2.50-3.50 | 4.50-6.50 | P/0.04, S/0.03, Cu/0.10-0.80 | 250 HB | Two-phase with Cr-Mo-Ni, resistant to Chloride Corrosion, heat resistant up to 300°C suitable for oil drilling-paper-biofuel production related industries |  | ||
 | 2507 | – | 1.4410, | – | 0.03 | 0.80 | 1.20 | 24.0-26.0 | 3.00-5.00 | 6.00-8.00 | P/0.035, S/0.02, Cu/0.50, | 270 HB | Two-phase, mixture of Cr-Mo-Ni, resistant to severe Chloride-Bearing Corrosion, heat limitation at 316°C, suitable for oil drilling-paper-sugar production such as propellers, axles, valves |  | ||
| 329J4L | A182 Gr F50/F61 | 1.4507, | SUS 329J4L | 0.03 | 1.00 | 1.50 | 24.0-26.0 | 2.50-3.50 | 5.50-7.50 | P/0.04, S/0.03, N/0.08-0.30 | 302 HB | Two-phase with ultra low C-Mo mixtures, resistant to Phosphoric-Acetic-Sulphuric Acids Corrosion, can maintain hardness at high temperature 950-1150°C |  | ||